I am currently working on a project with this stuff. I am finding all kinds of hard spots in this material (during a gundrill cycle, my spindle load will vary anywhere between 5 - 15% in a 9" deep hole....stays at 5% for an inch, climbs to 15%, back down to 5%, ect) Hard spots in the material would be very undesirable in the particular application that this part is for. (A bolt action receiver....hard spots could cause it to grenade)
I am wondering if we just came across a bad lot of material or if it common to see these issues with this Flexor-M