I was wondering if anyone has some experience burning moldmax that might have some tips or suggestions to help.
I have burned moldmax a few times but it has taken a really long time and I have had to double or even triple my electrode quantity due to wear.
We have 4 Charmilles sinkers and I will most likely be using the roboform 550 to burn these jobs. I'm not burning any ribs but I am burning a good amount of material.
Does anyone know if Charmilles has specific technology settings to burn this type of alloy? And what type of graphite would be best to use? I have read that Poco C3 (copper impregnated) might be the best choice but it's also very expensive.
Thank you in advance for your help.
I have burned moldmax a few times but it has taken a really long time and I have had to double or even triple my electrode quantity due to wear.
We have 4 Charmilles sinkers and I will most likely be using the roboform 550 to burn these jobs. I'm not burning any ribs but I am burning a good amount of material.
Does anyone know if Charmilles has specific technology settings to burn this type of alloy? And what type of graphite would be best to use? I have read that Poco C3 (copper impregnated) might be the best choice but it's also very expensive.
Thank you in advance for your help.