trumpeterjack
Plastic
- Joined
- May 14, 2006
- Location
- Oregon
I have never worked on sears or hammers (tumblers) before, but I believe that they both should be at least case hardened or hardened through, isn't that correct, meaning that they cannot be easily cut with a common file, is this correct? I have a pair of sears with hammers, that can be filed, so I believe that they are a bit on the soft side, so should be case hardened, at least, so I am thinking about case hardening them with Kasenite, do you think that would be the most appropriate thing to do?