  1. be careful, iron at orange-red is pretty...

    be careful, iron at orange-red is pretty bendable. make sure it is well supported while at temperature.



    dee
    ;-D
  2. If you are going to heat treat it, you should...

    If you are going to heat treat it, you should soak it at 1020F to 1200F one hour/inch thickness. when you pull it out you could just braze it it will be hot enough to melt the brazing rod, you may...